Manganese Bronze Alloy C67300
Copper Alloy No. C67300
Manganese Silicon Bronze , CDA 673
Chemical Composition % by weight
Manganese Silicon Bronze , CDA 673
Chemical Composition % by weight
Element | Nominal | Minimum | Maximum |
Copper | 60.5 | 58 | 63 |
Lead | 1.7 | .40 | 3 |
Iron | - | - | .50 |
Tin | - | - | .30 |
Zinc | Remainder | ||
Nickel (incl. Co) | - | - | .25 |
Aluminum | - | - | .25 |
Manganese | 2.75 | 2 | 3.5 |
Silicon | 1 | .5 | 1.5 |
Applications
Hydraulic piston shoes, cylinder liners, cams.
Common Fabrication Processes
Machining
Mechanical Properties
Typical for 2" Bar As Extruded Temper
Hardness* | Rockwell B Scales | 78 |
Tensile Strength** | KSI | 75 |
Yield Strength** (.5% EAU) | KSI | 36 |
Elongation** | % in 2 inch | 26 |
**Test values are nominal approximations and depend on specimen size and orientation.
Physical Properties
Thermal Conductivity | BTU/ (sq ft-ft-hr-F) | 58 |
Specific Heat | BTU/lb/ºF @ 68F | .09 |
Thermal Expansion | Per °F from 68 F to 572 F | .000011 |
Density | lb/cu in @ 68 F | .293 |
Electrical Conductivity* (Annealed) | % IACS @ 68 F | 23 |
Modulus of Elasticity (Tension) | KSI | 16,000 |
*Volume basis
Fabrication Properties
Capacity for being cold worked | Fair |
Suitability for being joined by: | Soldering/Good |
Brazing/Not Recommended | |
Oxyacetylene Welding/Not Recommended | |
Gas Shielded Arc Welding/Fair | |
Coated Metal Arc Welding/Not Recommended | |
Resistance Welding | Spot/Good |
Seam/Good | |
Butt/Good |