Copper Alloy No. C95600
Copper Alloy No. C95600
Aluminum Bronze CDA 956
Chemical Composition % by weight
Aluminum Bronze CDA 956
Chemical Composition % by weight
Element | Nominal | Minimum | Maximum |
Copper | 90.3 | 88 | Rem. |
Lead | - | - | - |
Iron | - | - | - |
Nickel (incl Co) | - | - | .25 |
Aluminum | 7 | 6 | 8 |
Manganese | - | - | - |
Magnesium | - | - | - |
Silicon | 2.5 | 1.8 | 3.2 |
Zinc | - | - | - |
Tin | - | - | - |
Applications
Cable connectors, pole line hardware, terminals, gears, worm gears, marine hardware, valve stems.
M07 - As Continuous Cast
Hardness* | Brinell Hardness (3000 kg load) | 140 |
Tensile Strength** | KSI | 75 |
Yield Strength ** | KSI (0.5% Ext. under load) | 34 |
Elongation** | % in 2 inch | 18 |
**Test values are nominal approximations and depend on specimen size and orientation.
Physical Properties
Thermal Conductivity | BTU/ (sq ft-ft-hr-F) | 22.3 |
Specific Heat | BTU/lb/ºF @ 68F | .09 |
Thermal Expansion | Per °F from 68 F to 572 F | .000009 |
Density | lb/cu in @ 68 F | .278 |
Electrical Conductivity | % IACS @ 68 F | 8 |
Modulus of Elasticity | KSI | 15,000 |
*Volume basis
Fabrication Practices
Stress relieving temperature | 600 F or 315 C |
Time at temperature | 1 hour per inch of section thickness |
Responds to heat treatment | Yes |
Solution heat treating temperature | 1600-1675 F or 870-910 C |
Time at temperature | 1 hour per inch of section thickness |
Quenching medium | Water |
Annealing temperature | 1150-1225 F or 620-660 C |
Time at temperature | 1 hour per inch of section thickness |
Machinability rating (Free Cutting Brass=100) | 60 |
Suitability for being joined by: | Soldering/Good |
Brazing/Good | |
Oxyacetylene Welding/Not Recommended | |
Gas Shielded Arc Welding/Good | |
Coated Metal Arc Welding/Fair |